Product Listing - Atlas-Fluoride Releasing Crown and Bridge Cement (Dual-Cure, Auto-Mix System)

Atlas-Fluoride Releasing Crown and Bridge Cement (Dual-Cure, Auto-Mix System)

Untitled 1

Atlas is used for: final cementation of implant prosthesis, crowns, bridges, in-lays, on-lays, Maryland bridges, veneers, cementation of posts and pins, pit and fissure sealants, periodontal splinting, and cementation of orthodontic bands and appliances.

Fluoride release
X-ray opacity
Excellent handling characteristics
Low irritation potential
Negligible solubility
Low film thickness
Excellent resistance to oral environment and mechanical strength assure good long-term performance
Long shelf-life

PRODUCT SPECIFICATIONS
*Typical Composition*
Resin based BIS-GMA, radio opaque glass filler, pyrogenic silica, catalyst, stabilizers, and pigments
Total filler content (by weight)	61%
Total filler content (by volume)	41%
Specific gravity	1.72 g/cm3
*Working Properties*
Mixing time	Auto-Mix System
Working time (incl. mixing time; (23 �C); 74�F	> 90 sec
Depth of light cure	> 1,75 mm*
Self-cured mode (37 �C); 99 �F;	3:00 min
*Physical Properties*
Flexural (transverse) strength	130 Mpa
Flexual modules	5000 MPa
Compressive strength	55 MPa
Diametral tensile strength	52 MPa
Water sorption	< 20 �g/mm3
Water solubility	< 5 �g/mm3
Color stability	very good
Barcol hardness	70
Radio opacity	ca. 250% Al

* the measured value (height of the cylinder of cured material) divided by two, according to ISO 4049

Price: US$ 180.00

Special Offer: order second Atlas kit at a discount:

L/C Filling Materials-Acorn	Orthodontic Adhesives	Corded/Cordless LED Light
S/C Filling Material-Acclaim	Temporary Cements	Porcelain Repair Material
Flowable Composite (L-Sha)	Temporary Restorative	Teeth Whitening System
Core Build-Up Materials	Liners	Glass Ionomer
Cements	Z Bond Dentin/Enamel Bonding Agent	Etch Gel
Dental Diamond Instruments	Enamel Bonding Agents